PVA high - strength high - modulus fiber

Contact us

PVA high - strength high - modulus fiber mainly take polyvinyl alcohol as raw material. It ‘s good at acidproof, alkaliproof, abrasion resistance, sunlight resistance, with high strength and high modulus, its aggregate index is much better than common standard product. It’s mainly used in the field of industry fabric, building material reinforcement, package material, high property rope, net. Etc.

A. main usage: . concrete reinforce material used for building

.. ideal replacement of cement and glass fiber

.. reinforce material for inner wall decorate fiber

.. high strength fishing net,cable,safty net

.. high strength industry used fabric

.. modern package reinforce material

 

B.   main specification and property:

item /property

high strength & modulus 1.

High strength & modulus 2.

Super fiber 1. For building material

super fiber 2. For building material

density (g/cm2)

1.26

1.26

1.26

1.26

titre (dtex)

2.0 /0.3

2.0/0.3

1.7 - 3.0

1.7 - 3.0

length (mm)

2 - 65

2 - 65

2 - 65

2 - 65

tenacity (CN/dtex)

> 10.5

> 10.5

8

6

yang’s modulus (CN/dtex)

> 240

> 240

>200

>150

breaking elongation (%)

< 7+/-1.5

<7+/-1.5

 

 

reducing quantity of hot water

< 2

< 3

 

 

acid proof

good

good

good

good

alkali resistant

good

good

good

good

ultraviolet lay resistant

good

good

good

good

electric conductivity

low

low

low

low

heat conduction

low

low

low

low

C.   fiber breaking elongation comparison

 

 

 

 

 

 

 

 

fiber

vinylon-high strength

vinylon-common standard

nylon

PP fiber

polyester (common standard)

polyester (high strength)

breaking elongation %

7

15

20 - 40

15 - 35

14 - 25

10 - 14

 

D.   alkali resistance comparison:

 

test condition

fiber strength lossing rate (%)

density%

temperature

time(h)

vinylon-high

man-made yarn

nylon 6

PET

1

20

10

0

12

0

1

1

100

100

7

29

25

71

40

20

10

0

100

18

4

 

E.    sunshine resistance comparison:

 

dry in the sun (hour)

fiber strength losing rate ( % )

high strength vinylon

nylon 6

viscose fiber

cotton

100

3.05

19.6

4.26

3.67

300

7.93

41.2

7.45

30.73

500

10.98

65.09

25.00

38.53

700

11.16

74.51

63.30

49.54

 

F. USAGE IN ASBESTOS CEMENT PRODUCT OF PVA HIGH STRENGTH & MODULUS

 

SHORTCOMING OF THE MAIN REINFORCE MATERIAL:

 

1.     ASBESTOS – harmful to health, polluting circumstances

o        acting as a reinforce material, asbestos has a small tenacity,easy to break.

o        with property of acid resistant but not alkali proof.

 

2.     GLASS FIBER - high price

 

PVA HIGH STRENGTH & MODULUS FIBER IS THE IDEAL REPLACEMENT OF ASBESTOS AND GLASS FIBER:

advantage: a. good physical and chemical property.

a.     excellent mechanics property, can obviously improve the board’s toughness and the anti-shock ability, reduce break rate.

a.     with stable quality and good disperse property.

b.     with good alkali & acid resistant property, suitable for each type of cement.

c.      improve the board’s anti-crook temperature, reducing product volume.

d.     improve environment.

e.      no need to reform the original equipment, can used in the common process.

f.       the product fits the international BG9772-88.

 

G.   SUGGEST USAGE FORMULA:

 

1.     small corrugated tile: :

unit

cement

asbestos

vinylon

pulp

sepiolite

addition

ratio of replace asbestos

quantity of replace asbestos

KG

250

26

4.7

6

just the right amount

just the right amout

1: 4.5

-

%

87.2

9.1

1.64

2.1

-

-

-

40

 

 

2) cement plate

unit

cement

asbestos

vinylon

sepiolite

pulp

quantity of replace asbestos

KG

250

15

4.7

30

6

-

%

81.78

4.91

1.54

9.81

1.96

70

 

H. USAGE IN THE BUILDING CONCRETE OF PVA HIGH STRENGTH&MODULUS

1.     structure tortoise-crack in concrete

o        in the concrete industry, the reason of tortoise-crack is of the inner pressure surpassed it should beard tenacity. To strength the structure tenacity can reduce the pressure coming outside, but can’t be controlled effectively because of the inner pressure when shrinkage. In the period of molding, the tortoise-crack happened and formed within 24 hours because of inner dry shrinkage coming from the concrete.

 

2.     available method:

to mix the pva high-strength & modulus fiber as the main or next reinforce material can improve the building material’s anti-draw ability and toughness. It can increase the concrete’s ability of tension resistance, reducing water losing rate, improving the concrete material’s ability of anti-breaking, effectively controlling the tortoise crack.

3.     purpose of using the fiber:

restrain tortoise crack

increase tenacity,anti-breaking,wear and tear.

Increase weary resistance of anti-elasticity.

Reduce water oozing.

Extend the concrete life.

4.     good property:

good dispersing ability, can dispersed in each part evenly.

Suitable for the concrete place which can’t have metal.

No corrode, without chemical function.

Excellent ability of anti-alkali, suitable for any type of cement.

Doesn’t affect the concrete surface property.

Improve working environment.

No need to increase any equipment.

I. ADVISE MIXING QUANTITY:

1.        used as lime applying material: 300g fiber/m3 building material .

2.     used as inner wall decorating material: 300 g fiber/m3 .

used as concrete strength material: 600 g fiber/ m3 concrete

***************************************************************

北京中纤新纶电子商务有限公司

邮编:100025 北京市,朝阳区,延静里中街3号院,5号楼(泰公寓)208

电话:010-84042763,传真:010-84035346

ChinaFiber XinLun

Rm.208, Kai-Tai Mansion, Building No.5, Yard No.3, Yan-Jing-Li Middle-Str., Chao-Yang District, Beijing 100025 China.

Tel: +86 10 84042763, Fax: +86 10 84035346,

www.chinafiber.com  E-Mail: sales@chinafiber.com

***************************************************************

Back homepage 返回上一页